Tilara Polyplast PMMA Sheet

TPPLGLAS® XT Acrylic Sheet

Tilara Polyplast xt-acrylic Sheeet

TPPLGLAS XT Acrylic Sheet, Manufactured by Tilara Polyplast Pvt Ltd. is a thermoplastic sheet that is an alternative of Polycarbonate when extreme strength is not compulsory. It is often preferred because of its moderate properties, easy handling, fabrication and other processing. TPPLGLASS XT Acrylic Sheet has better scratch resistance properties than other conventional sheet.
TPPLGLAS XT Acrylic Sheet manufactured by modified grade MMA resin which has higher scratch resistance with best impact resistance, weather resistance and thermal resistance. As per it's better weather and UV resistance, it’s also perfect for outdoor application. It has transmittance up to 92% of visible light and give best reflection from each of its surface. Our moderate extrusion technology process maintains product quality like transparency, color, accurate thickness and other object.
TPPLGLAS XT Acrylic Sheet can be glue easily by using many different organic based adhesive. Being transparent, Color and durable, it is a multifaceted material and used in various segment and applications such as sound barrier walls, Bathtubs, Security barrier, Shatter resistance panels for building window, Furniture, Lighting, Sign-Display, advertising and many other.
TPPLGLAS XT Acrylic Sheet is odorless that can be easily thermoform, blow, bend, print and laser without any excruciation.

APPLICATIONS

  • Exhibition Booths
  • Interior and Exterior Lighting
  • Cosmetics
  • Museum Casings
  • Noise-reducing Walls
  • Signage and Advertising
  • Aquarium
  • Gift Articles and Trophy

KEY FEATURES

  • Excellent thickness tolerance
  • Optical Clarity
  • Light weight
  • High gloss surface on both sides
  • Hard wearing
  • Weather resistant
  • Easy to bend and shape
  • Economical
  • Suitable for vacuum forming

TPPLGLAS XT Acrylic Sheet

GENERAL
General Properties Conditions Test Method Unit Value
Density ISO 1183 g/cm3 1,19
Water Absorption (24h) 23 °C / 50% RH (24h) ISO 62 % 0,3
Moulding Shrinkage ASTM D-955 % 0,2-0,6
MECHANICAL
General Properties Conditions Test Method Unit Value
Tensile Strength at Break 23 °C ISO 527-2 MPa 83
Elongation at Break 23 °C ISO 527-2 % 7
Tensile Modulus 23 °C ISO 527-2 MPa 3200
Flexural Strength at Break 23 °C ISO 178 MPa 120
Flexural Modulus 23 °C ISO 178 MPa 330
Charpy Impact Strength with Notched 23 °C ISO 178-1ea kj/m2 2
Izod Impact notched ISO 178 kj/m22,1
Rockwell Hardness M Scale ISO 2039-2 M-scale92
THERMAL
General Properties Conditions Test Method Unit Value
Vicat Temperature 50 N ISO 306 °C 105
Deflection temperature under load 1,8 MPa ISO 75 °C 100
Coefficient of linear expansion ISO 11359-2 mm/m°C 0,07
THERMAL
General Properties Conditions Test Method Unit Value
Dielectric Strength DIN53481 kV/mm 20
Dielectric Constant 1 KHz DIN53843 3,1

AVAILABLE IN

Thickness: 2mm to 12mm

Colour: Clear, 0-40, White & Black (customise are available on request)

Width: Upto 2100mm